LOW-PERM URETHANE
|
|
FOAMFLEX #1718
|
|
|
PROPERTY
|
SPECIFICATION
|
TEST METHOD
|
|
|
|
|
Composition
|
Polyether PolyUrethane
|
|
|
|
Cell Structure
|
Open
|
|
|
|
Density (pcf)
|
1.75 to 2.15
|
ASTM D3574-91
|
|
|
Compression Deflection
(psi)
|
|
ASTM D3574-91
|
 |
|
25%
|
0.15
|
|
|
|
50%
|
0.20
|
|
|
|
Compression Set
50%
(% loss)
|
15
|
ASTM D3574-91
|
|
|
Tensile Strength
(psi)
|
9 min
|
ASTM D3574-91
|
|
|
Elongation (%)
|
125
|
ASTM D3574-91
|
|
|
Tear Resistance
(ppi)
|
1
|
ASTM D3574-91
|
|
|
Flame Resistance
|
Pass
|
FMVSS 302,
CAL 117A
|
|
|
Pressure Pot
(psi)
|
1.45
|
ASTM D3574-91
|
|
|
This
product is certified to meet the following
automotive specifications:
FORD .... ESA-M4D-200B
CHRYSLER .... MSAY-326A
GM .... GM251M Type 1 |
|
| Jacobs
and Thompson cannot anticipate all conditions
under which this information and our products
of other manufacturers in combination with
our products, may be used. We accept no responsibility
for results obtained by the application of
the information or the safety and suitability
of our products, either alone or in combination
with other products. Unless otherwise agreed
in writing, we sell the products without warranty
and users are advised to make their own tests
to determine the safety and suitability of
each such product combination for their own
purpose. |
|
|
|
|
|
|
Questions, Comments
or Suggestions?
|
|
|
webmaster@foamparts.ca
|
|
|
|
 |
|
|
|
|
Vinyl Nitrile
|
|
|
1210,
1212
|
|
 |
|
|
Neoprene Blends
(CR/EPT/SBR)
Closed Cell
|
|
|
1220,
1240,
1260
|
|
|
|
|
Expanded PVC
|
|
|
1307,
1388,
1357,
1391,
1376
|
|
|
|
|
|
Expanded EPDM
Closed Cell
|
|
|
|
1402,
1440
|
|
|
|
|
|
|
|
Micro Cellular
PolyUrethane
|
|
|
|
6153,
6204,
6256
|
|
|
|
|
|
|
|
Polyester Urethane
Open Cell
|
|
|
|
1820,
1840,
1860
|
|
|
|
|
|
|
|
Low Perm Urethane
|
|
|
|
1830,
1718
|
|
|
|
|
|
|
|
PolyEthylene
|
|
|
|
2542E,
2544A
|
|
|
|
|
|
|
|
EVA
|
|
|
|
2720
|
|
|
|
|
|
|
|
Felt/Flocked Felt
|
|
|
|
1990,
7425
|
|
|
|
|
|
|
|
Speciality Products
|
|
|
|
5215,
1224
|
|
|
|
|
|
|
|
Polyether Urethane
Open Cell
|
|
|
|
1727,
1735
|
|
|
|
|
|
|