EVA
|
|
FOAMFLEX #2720
|
|
|
PROPERTY
|
SPECIFICATION
|
TEST METHOD
|
|
|
|
|
Composition
|
EVA
|
|
|
|
Density (pcf)
|
1.5 to 2.5
|
ASTM D3574
|
|
|
25% CFD (psi)
|
3 to 7
|
ASTM D1056
|
|
|
Compression Set
(% loss)
|
35
|
ASTM D1056
|
|
|
Tensile Strength
(psi)
|
50
|
ASTM D412
|
|
|
Elongation (%)
|
200
|
ASTM D412 (Die
A)
|
|
|
Tear Strength
(ppi)
|
10
|
ASTM D624
|
|
|
Durometer Shore
00
|
30 to 50
|
ASTM D2240
|
|
|
Resilience (%)
|
45
|
ASTM D2632
|
|
|
Accelerated Aging
7d @ 158†F
|
|
ASTM D1056
|
 |
|
Flexibility (180†
bend)
|
Pass / No Cracking
|
|
|
|
Change in CFD
(%)
|
+/-30
|
|
|
|
Flame Resistance
|
Pass
|
FMVSS 302
|
|
|
Service Temperature
|
|
ASTM D746
|
|
|
Low
|
-70†F
|
|
|
|
High Continuous
|
160†F
|
|
|
|
High Intermittent
|
180†F
|
|
|
|
| Jacobs
and Thompson cannot anticipate all conditions
under which this information and our products
of other manufacturers in combination with
our products, may be used. We accept no responsibility
for results obtained by the application of
the information or the safety and suitability
of our products, either alone or in combination
with other products. Unless otherwise agreed
in writing, we sell the products without warranty
and users are advised to make their own tests
to determine the safety and suitability of
each such product combination for their own
purpose. |
|
|
|
|
|
|
Questions, Comments
or Suggestions?
|
|
|
webmaster@foamparts.ca
|
|
|
|
 |
|
|
|
|
Vinyl Nitrile
|
|
|
1210,
1212
|
|
 |
|
|
Neoprene Blends
(CR/EPT/SBR)
Closed Cell
|
|
|
1220,
1240,
1260
|
|
|
|
|
Expanded PVC
|
|
|
1307,
1388,
1357,
1391,
1376
|
|
|
|
|
|
Expanded EPDM
Closed Cell
|
|
|
|
1402,
1440
|
|
|
|
|
|
|
|
Micro Cellular
PolyUrethane
|
|
|
|
6153,
6204,
6256
|
|
|
|
|
|
|
|
Polyester Urethane
Open Cell
|
|
|
|
1820,
1840,
1860
|
|
|
|
|
|
|
|
Low Perm Urethane
|
|
|
|
1830,
1718
|
|
|
|
|
|
|
|
PolyEthylene
|
|
|
|
2542E,
2544A
|
|
|
|
|
|
|
|
EVA
|
|
|
|
2720
|
|
|
|
|
|
|
|
Felt/Flocked Felt
|
|
|
|
1990,
7425
|
|
|
|
|
|
|
|
Speciality Products
|
|
|
|
5215,
1224
|
|
|
|
|
|
|
|
Polyether Urethane
Open Cell
|
|
|
|
1727,
1735
|
|
|
|
|
|
|